In situ synthesis of Si<inf>3</inf>N<inf>4</inf> in the Na<inf>2</inf>SiF<inf>6</inf>-N<inf>2</inf> system via CVD: Kinetics and mechanism of solid-precursor decomposition

A. L. Leal-Cruz, M. I. Pech-Canul

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

20 Citas (Scopus)

Resumen

The kinetics of decomposition of Na2SiF6 in nitrogen to in situ synthesize Si3N4 was investigated. First, an optimization of the following parameters for the thermal decomposition was performed: nitrogen precursor (N2 or N2:NH3), processing time and temperature range. According to the analysis of variance (ANOVA), the optimum conditions to maximize the decomposition of Na2SiF6 are: N2, 120 min, and 465-873 K. Based on thermodynamic predictions and evidence on the synthesis of Si3N4 during the thermal decomposition, it is proposed that in nitrogen Na2SiF6 decomposes endothermically into various gaseous species (SiF4, SiF3, SiF2, SiF and Si) denoted as SiFx, through a series of complex reactions of zero-order with respect to the gaseous products, with activation energy of 156 kJ mol- 1 and a rate-determining-step given by the chemical reaction itself. The gaseous species are formed through a set of simultaneous reactions represented by the next general equation:Na2SiF6 → 2 NaF + SiFx(g) + n F2(g)Where x varies from 0 to 4 and n given by (2-0.5x) takes the values 0, 1/2, 1, 3/2 and 2. Silicon nitride is formed according to:3 SiFx(g) + 2 N2 → Si3N4 + m F2m = 1.5x and takes the values 6, 9/2, 3, 3/2 and 0. © 2006 Elsevier B.V. All rights reserved.
Idioma originalInglés estadounidense
Páginas (desde-hasta)3529-3536
Número de páginas8
PublicaciónSolid State Ionics
DOI
EstadoPublicada - 15 ene. 2007
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'In situ synthesis of Si<inf>3</inf>N<inf>4</inf> in the Na<inf>2</inf>SiF<inf>6</inf>-N<inf>2</inf> system via CVD: Kinetics and mechanism of solid-precursor decomposition'. En conjunto forman una huella única.

Citar esto