Obtaining of Mg-Zn Co-Doped GaN Powders via Nitridation of the Ga-Mg-Zn Metallic Solution and Their Structural and Optical Properties

Erick Gastellóu*, Rafael García, Ana M. Herrera, Antonio Ramos, Godofredo García, Gustavo A. Hirata, José A. Luna, Roberto C. Carrillo, Jorge A. Rodríguez, Mario Robles, Yani D. Ramírez, Guillermo Martínez

*Autor correspondiente de este trabajo

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

Resumen

Mg-Zn co-dopedGaN powders via the nitridation of a Ga-Mg-Zn metallic solution at 1000 °C for 2 h in ammonia flow were obtained. XRD patterns for the Mg-Zn co-dopedGaN powders showed a crystal size average of 46.88 nm. Scanning electron microscopy micrographs had an irregular shape, with a ribbon-like structure and a length of 8.63 µm. Energy-dispersive spectroscopy showed the incorporation of Zn (Lα 1.012 eV) and Mg (Kα 1.253 eV), while XPS measurements showed the elemental contributions of magnesium and zinc as co-dopant elements quantified in 49.31 eV and 1019.49 eV, respectively. The photoluminescence spectrum showed a fundamental emission located at 3.40 eV(364.70 nm), which was related to band-to-band transition, besides a second emission found in a range from 2.80 eV to 2.90 eV (442.85–427.58 nm), which was related to a characteristic of Mg-doped GaN and Zn-doped GaN powders. Furthermore, Raman scattering demonstrated a shoulder at 648.05 cm−1, which could indicate the incorporation of the Mg and Zn co-dopants atoms into the GaN structure. It is expected that one of the main applications of Mg-Zn co-doped GaN powders is in obtaining thin films for SARS-CoV-2 biosensors.

Idioma originalInglés
Número de artículo3272
PublicaciónMaterials
Volumen16
N.º8
DOI
EstadoPublicada - abr. 2023

Nota bibliográfica

Publisher Copyright:
© 2023 by the authors.

Huella

Profundice en los temas de investigación de 'Obtaining of Mg-Zn Co-Doped GaN Powders via Nitridation of the Ga-Mg-Zn Metallic Solution and Their Structural and Optical Properties'. En conjunto forman una huella única.

Citar esto